Non-aqueous inkjet ink and ink set

ABSTRACT

A non-aqueous inkjet ink includes a polyvinyl chloride resin synthesized by a suspension polymerization method or an emulsion polymerization method, an organic solvent that is a mixed solvent including diethylene glycol ethyl methyl ether, diethylene glycol diethyl ether, and diethylene glycol monoethyl ether in which the polyvinyl chloride resin is dissolved. This inkjet ink also includes a pigment, and a radical polymerization inhibitor. The radical polymerization inhibitor prevents the polyvinyl chloride resin from gelling in a short period and causing a discharge fault, clogging, etc. An ink set of inkjet inks includes a combination of the non-aqueous inkjet inks above having respective colors and including at least a cyan ink, a magenta ink, a yellow ink, and a black ink.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a Continuation application of co-pending U.S.application Ser. No. 12/929,557, filed on Feb. 1, 2011, which is hereinincorporated by reference.

BACKGROUND OF THE INVENTION

The present invention relates in particular to a non-aqueous inkjet inksuitable for printing images, characters, etc., on a surface of apolyvinyl chloride sheet, etc.

Conventionally, inkjet printing, with which images, characters, etc.,are printed by discharging an inkjet ink as microscopic droplets from anozzle of an inkjet printer, is favorably used for printing mainly ontopaper or other water-absorbing surface. As the inkjet ink for thispurpose, an aqueous inkjet ink having a water-soluble dye or othercolorant added therein is widely used in general.

However, recently, inkjet printing is being used to perform printingonto various surfaces, especially in business applications and invarious other fields. There is a demand for printing images andcharacters, not only with good image quality but also with good waterresistance, light resistance, friction resistance, etc., on the varioussurfaces.

For this purpose, non-aqueous inkjet inks that practically do notcontain water as a solvent and use only organic solvents, and inkjetprinters that use such inks are being put to practical use and becomingpopularly used in place of aqueous inkjet inks.

For example, a large-size inkjet printer for printing images andcharacters on a surface of a polyvinyl chloride sheet, etc., that isfrequently used as a medium, for example, for outdoor advertisements isbecoming popularly used.

As the non-aqueous inkjet ink used in the inkjet printer, an inkcontaining a pigment with excellent light resistance, a binder resin forfixing the pigment onto a surface of a polyvinyl chloride sheet, etc.,and an organic solvent capable of dissolving the binder resin is mainlyused.

As the binder resin, any of various resins that are excellent in fixingproperty with respect to the surface of a polyvinyl chloride sheet,etc., such as an acrylic resin, polyester resin, polyurethane resin,polyvinyl chloride resin, nitrocellulose resin, etc., is used, and amongthese, a polyvinyl chloride resin, which is best in fixing property, isused favorably.

Also, by copolymerizing vinyl acetate with vinyl chloride, thesolubility in the organic solvent can be improved, and images andcharacters printed on the surface of the polyvinyl chloride sheet can beincreased in flexibility to improve scratch resistance of a print. Avinyl chloride-vinyl acetate copolymer is thus used especially favorablyas the polyvinyl chloride resin.

A non-aqueous inkjet ink using a vinyl chloride-vinyl acetate copolymeror other polyvinyl chloride resin is described, for example, in JP2004-231870A, JP 2005-23298A, JP 2005-200469A, etc.

Also, a metal coordination compound or other additive is added in anon-aqueous inkjet ink.

A surface of a nozzle plate, etc., making up a nozzle of an inkjetprinter must have a property of appropriately repelling a non-aqueousinkjet ink in order to discharge the non-aqueous inkjet inksatisfactorily through the nozzle.

A coating film having a property of repelling the non-aqueous inkjet inkis thus formed on the surface of the nozzle plate, etc. As the coatingfilm, a eutectoid coating film of a fluororesin and nickel, etc., isused.

The metal coordination compound coordinates to the nickel in theeutectoid coating film and thereby functions to improve resistance ofthe eutectoid coating film against the organic solvent contained in thenon-aqueous inkjet ink.

Nitrogen-containing compounds, such as imidazoles, benzotriazoles, etc.,can be cited as examples of the metal coordination compound.

SUMMARY OF THE INVENTION

Conventionally, as the polyvinyl chloride resin, that synthesized by asolution polymerization method is generally used. However, with thesolution polymerization method, a large amount of an organic solventmust be used in synthesizing the polyvinyl chloride resin and treatmentthereof is a problem.

That is, an easiest method for taking out the synthesized polyvinylchloride resin from inside a reaction system is to remove the organicsolvent by performing a drying process, that is, by letting the organicsolvent evaporate into air. However, recently, in consideration oflightening an environmental load, it is becoming necessary to recoverthe organic solvent by an exhaust treatment, waste liquid treatment,etc., and thereby avoid letting the organic solvent evaporate into airas much as possible.

Equipment required for such treatments, energy required for operation ofsuch equipment, etc., lower productivity of polyvinyl chloride resin andcause rise of production cost.

Use of a polyvinyl chloride resin synthesized by a suspensionpolymerization method or emulsion polymerization method that does notrequire the use of a large amount of an organic solvent as in thesolvent polymerization method is thus being examined.

However, examination by the present inventor showed that a non-aqueousinkjet ink prepared using a polyvinyl chloride resin synthesized byeither of these methods tends to gel within a short period in comparisonto a polyvinyl chloride resin synthesized by the conventional solutionpolymerization method.

Gelling occurs especially readily in a case of storage upon vacuumfilling in a bag made of an aluminum laminate material, etc., that isgenerally used as a means for supplying ink to a large-size inkjetprinter.

When the polyvinyl chloride resin gels, it becomes difficult for apredetermined amount of the ink to be discharged appropriately throughthe nozzle of the inkjet printer or the nozzle becomes clogged so thatthe ink cannot be discharged at all. A problem that images, characters,etc., of satisfactory image quality cannot be printed thus occurs.Gelling of the polyvinyl chloride resin must be suppressed as much aspossible.

An object of the present invention is to provide a non-aqueous inkjetink, which contains a polyvinyl chloride resin synthesized by asuspension polymerization method or an emulsion polymerization methodand yet with which there is no possibility of the polyvinyl chlorideresin gelling within a short period and thereby causing a dischargefault, clogging, etc., and an ink set that includes the non-aqueousinkjet ink.

The inventor examined causes as to why a polyvinyl chloride resinsynthesized by the suspension polymerization method or the emulsionpolymerization method gels within a short period. As a result, theinventor found that one cause of gelling readily is that the polyvinylchloride resin synthesized by the suspension polymerization method orthe emulsion polymerization method is high in a residual amount ofunreacted monomer in comparison to a resin synthesized by the solutionpolymerization method.

That is, as is well known, the oxygen contained in air acts as apolymerization inhibitor of a radical polymerization reaction. However,when a non-aqueous inkjet ink is vacuum filled in the bag and air is cutoff, a state in which the unreacted monomer undergoes the radicalpolymerization reaction readily is entered.

A thermal history, etc., during storage after filling in the bag thenacts as a trigger that starts the radical polymerization reaction, andgelling of the polyvinyl chloride resin and various accompanyingproblems occur more readily the greater the residual amount of theunreacted monomer.

Also, by examination by the inventor, it was found that especially whenthe non-aqueous inkjet ink contains a basic component with a pH inexcess of 9, the basic component promotes the radical polymerizationreaction and the accompanying gelling of the polyvinyl chloride resin.

By further examination, the inventor found that making a radicalpolymerization inhibitor having a function of inhibiting the radicalpolymerization reaction be contained in the non-aqueous inkjet ink inadvance is especially effective for preventing gelling.

The present invention thus provides a non-aqueous inkjet ink including apolyvinyl chloride resin synthesized by a suspension polymerizationmethod or an emulsion polymerization method, an organic solvent fordissolving the polyvinyl chloride resin, a pigment, and a radicalpolymerization inhibitor.

Although a radical polymerization inhibitor is a known component, thatthe radical polymerization inhibitor

(a) is included in the non-aqueous inkjet ink containing the polyvinylchloride resin, with which the polymerization reaction is completed andfurther polymerization reaction, crosslinking reaction, etc., is notpresumed, and

(b) thereby prevents a radical polymerization reaction of an unreactedmonomer that causes gelling of the polyvinyl chloride resin, and

(c) further that the cause of gelling of the polyvinyl chloride resin isthe unreacted monomer contained at a large amount especially in thepolyvinyl chloride resin synthesized by the suspension polymerizationmethod or the emulsion polymerization method, etc., are facts found forthe first time and clarified for the first time by the inventor incompleting the present invention and are by no means known facts.

As the radical polymerization inhibitor, at least one type selected fromthe group consisting of hydroquinones, catechols, hindered amines,phenols, phenothiazines, and condensed aromatic ring quinones can becited.

As is done conventionally, the non-aqueous inkjet ink may contain ametal coordination compound or other additive. Benzotriazoles arepreferable as metal coordination compounds. In addition to beingexcellent in function as metal coordination compounds, thebenzotriazoles do not exhibit basicity and thus do not have apossibility of promoting a radical polymerization reaction.

In a cyan non-aqueous inkjet ink that uses a phthalocyanine pigment asthe pigment, it is preferable to use a hindered amine as the radicalpolymerization inhibitor. A content proportion of the hindered amine ispreferably no less than 0.2 mass % and no more than 2 mass % of a totalamount of the non-aqueous inkjet ink.

In a magenta non-aqueous inkjet ink that uses a quinacridone pigment asthe pigment, it is preferable to use a hindered phenol as the radicalpolymerization inhibitor. The content proportion of the hindered phenolis preferably no less than 0.05 mass % and no more than 2 mass % of thetotal amount of the non-aqueous inkjet ink.

In a yellow non-aqueous inkjet ink that uses a chelate azo pigment asthe pigment, it is preferable to use a hindered amine as the radicalpolymerization inhibitor. The content proportion of the hindered amineis preferably no less than 0.05 mass % and no more than 2 mass % of thetotal amount of the non-aqueous inkjet ink.

In a black non-aqueous inkjet ink that uses carbon black as the pigment,it is preferable to use a hindered amine as the radical polymerizationinhibitor. The content proportion of the hindered amine is preferably noless than 0.05 mass % and no more than 2 mass % of the total amount ofthe non-aqueous inkjet ink.

The organic solvent is preferably a mixed solvent of diethylene glycolethyl methyl ether and

at least one type of solvent selected from the group consisting ofdiethylene glycol diethyl ether, tetraethylene glycol dimethyl ether,and propylene glycol dimethyl ether.

Also, the mixed solvent may further contain at least one type of solventselected from the group consisting of ethylene glycol monobutyl ether,diethylene glycol monoethyl ether, triethylene glycol monomethyl ether,propylene glycol monobutyl ether, dipropylene glycol monomethyl ether,dipropylene glycol dimethyl ether, and tripropylene glycol dimethylether.

The present invention provides an ink set that includes at leastnon-aqueous inkjet inks of respective colors of cyan, magenta, yellow,and black and with which the non-aqueous inkjet ink of at least one ofthe respective colors is the non-aqueous inkjet ink according to thepresent invention.

By the present invention, a non-aqueous inkjet ink, which contains apolyvinyl chloride resin synthesized by a suspension polymerizationmethod or an emulsion polymerization method and yet with which there isno possibility of the polyvinyl chloride resin gelling within a shortperiod and thereby causing a discharge fault, clogging, etc., and an inkset that includes the non-aqueous inkjet ink can be provided.

DETAILED DESCRIPTION OF THE INVENTION <<Non-Aqueous Inkjet Ink>>

A non-aqueous inkjet ink according to the present invention ischaracterized in including a polyvinyl chloride resin synthesized by asuspension polymerization method or an emulsion polymerization method,an organic solvent for dissolving the polyvinyl chloride resin, apigment, and a radical polymerization inhibitor.

<Polyvinyl Chloride Resin>

As the polyvinyl chloride resin, any of various polyvinyl chlorideresins synthesized by the suspension polymerization method or theemulsion polymerization method may be used. In particular, a vinylchloride-vinyl acetate copolymer synthesized by the suspensionpolymerization method or the emulsion polymerization method ispreferable as the polyvinyl chloride resin. When vinyl chloride iscopolymerized with vinyl acetate, solubility in the organic solvent canbe improved, and images and characters printed on a surface of apolyvinyl chloride sheet, etc., can be increased in flexibility toimprove scratch resistance of a print.

A molecular weight, vinyl acetate content, etc., of the vinylchloride-vinyl acetate copolymer may be set as suited.

For example, a vinyl chloride-vinyl acetate copolymer synthesized by thesuspension polymerization method has a number average molecular weightMn of preferably no less than 5000 and especially preferably no lessthan 10000, and preferably no more than 100000 and especially preferablyno more than 30000.

When the number average molecular weight Mn is less than the aboverange, a fixing property of the vinyl chloride-vinyl acetate copolymerwith respect to the polyvinyl chloride sheet decreases and the scratchresistance, etc., of the print may decrease.

On the other hand, when the above range is exceeded, the non-aqueousinkjet ink becomes too high in viscosity and it may not be possible tosatisfactorily discharge the non-aqueous inkjet ink as droplets througha nozzle of an inkjet printer.

Also, the vinyl acetate content of the vinyl chloride-vinyl acetatecopolymer is preferably no less than 1 mass %, more preferably no lessthan 10 mass %, and especially preferably no less than 13 mass %, andpreferably no more than 36 mass %, more preferably no more than 22 mass%, and especially preferably no more than 15 mass %.

When the vinyl acetate content is less than the above range, asolubility of the vinyl chloride-vinyl acetate copolymer particularly ina first organic solvent to be described below decreases so thatprecipitation occurs readily and the non-aqueous inkjet ink may therebydecrease in stability.

On the other hand, when the above range is exceeded, the fixing propertyof the vinyl chloride-vinyl acetate copolymer with respect to thepolyvinyl chloride sheet decreases and the scratch resistance, etc., ofthe print may decrease.

Examples of the vinyl chloride-vinyl acetate copolymer synthesized bythe suspension polymerization method include one type or two or moretypes among

SOLBIN CL (number average molecular weight Mn: 25000, vinyl acetatecontent: 14 mass %),

SOLBIN CNL (number average molecular weight Mn: 12000, vinyl acetatecontent: 10 mass %),

SOLBIN C5R (number average molecular weight Mn: 27000, vinyl acetatecontent: 21 mass %),

SOLBIN AL (number average molecular weight Mn: 22000, vinyl acetatecontent: 2 mass %),

SOLBIN TA5R (number average molecular weight Mn: 28000, vinyl acetatecontent: 1 mass %),

SOLBIN TA0 (number average molecular weight Mn: 15000, vinyl acetatecontent: 2 mass %),

SOLBIN TA3 (number average molecular weight Mn: 24000, vinyl acetatecontent: 4 mass %), etc.,

which are vinyl chloride-vinyl acetate copolymers of the SOLBIN(registered trademark) series manufactured by Nissin Chemical IndustryCo., Ltd.

A vinyl chloride-vinyl acetate copolymer synthesized by the emulsionpolymerization method has a weight average molecular weight Mw ofpreferably no less than 5000, more preferably no less than 30000, andespecially preferably no less than 45000, and preferably no more than100000, more preferably no more than 60000, and especially preferably nomore than 55000.

When the weight average molecular weight Mw is less than the aboverange, the fixing property of the vinyl chloride-vinyl acetate copolymerwith respect to the polyvinyl chloride sheet decreases and the scratchresistance, etc., of the print may decrease.

On the other hand, when the above range is exceeded, the non-aqueousinkjet ink becomes too high in viscosity and it may not be possible tosatisfactorily discharge the non-aqueous inkjet ink as droplets througha nozzle of an inkjet printer.

Also, the vinyl acetate content of the vinyl chloride-vinyl acetatecopolymer is preferably no less than 1 mass %, more preferably no lessthan 10 mass %, and especially preferably no less than 14 mass %, andpreferably no more than 36 mass %, more preferably no more than 20 mass%, and especially preferably no more than 16 mass %.

When the vinyl acetate content is less than the above range, thesolubility of the vinyl chloride-vinyl acetate copolymer particularly inthe first organic solvent to be described below decreases so thatprecipitation occurs readily and the non-aqueous inkjet ink may therebydecrease in stability.

On the other hand, when the above range is exceeded, the fixing propertyof the vinyl chloride-vinyl acetate copolymer with respect to thepolyvinyl chloride sheet decreases and the scratch resistance, etc., ofthe print may decrease.

Examples of the vinyl chloride-vinyl acetate copolymer synthesized bythe emulsion polymerization method include one type or two or more typesamong

VINNOL E15/45 (weight average molecular weight Mw: 45000 to 55000, vinylacetate content: 15.0±1.0 mass %),

VINNOL H14/36 (weight average molecular weight Mw: 30000 to 40000, vinylacetate content: 14.4±1.0 mass %),

VINNOL H15/42 (weight average molecular weight Mw: 35000 to 50000, vinylacetate content: 14.0±1.0 mass %),

VINNOL H40/43 (weight average molecular weight Mw: 40000 to 50000, vinylacetate content: 34.3±1.0 mass %),

VINNOL E15/45M (weight average molecular weight Mw: 50000 to 60000,vinyl acetate content: 15.0±1.0 mass %),

VINNOL E15/40M (weight average molecular weight Mw: 40000 to 50000,vinyl acetate content: 15.0±1.0 mass %), etc.,

which are vinyl chloride-vinyl acetate copolymers of the VINNOL(registered trademark) series manufactured by Wacker Chemie AG.

The content proportion of the polyvinyl chloride resin with respect tothe total amount of the non-aqueous inkjet ink is preferably no lessthan 1 mass % and especially preferably no less than 3 mass %, andpreferably no more than 10 mass % and especially preferably no more than7 mass %.

When the content proportion is less than the above range, the effect dueto containing of the polyvinyl chloride resin, that is, the effect offixing the pigment onto a surface of a polyvinyl chloride sheet, etc.,cannot be obtained adequately and the scratch resistance of the printmay decrease.

On the other hand, when the content proportion exceeds the above range,the non-aqueous inkjet ink becomes too high in viscosity and it may notbe possible to satisfactorily discharge the non-aqueous inkjet ink asdroplets through a nozzle of an inkjet printer.

<Organic Solvent>

As the organic solvent, any of various organic solvents that cansatisfactorily dissolve the polyvinyl chloride resin may be used.Aprotic polar solvents, such as N-methyl-2-pyrrolidone and othernitrogen-containing heterocyclic compounds and γ-butyrolactone and otheroxygen-containing heterocyclic compounds, etc., can be cited as examplesof the organic solvent. However, an aprotic polar solvent may degradethe above-described eutectoid coating film of a fluororesin and nickelin a short period. Also, an aprotic polar solvent has a possibility ofreadily causing gelling of the polyvinyl chloride resin.

As the organic solvent, it is preferable to use an alkylene glycolderivative that does not readily cause the gelling and with which thereis no possibility of degrading the eutectoid coating film, etc., in ashort period.

Also, as the organic solvent, it is further preferable to use, fromamong the below-described three types of first to third organic solventsthat are all alkylene glycol derivatives, a mixed solvent of the twotypes of the first and second organic solvents or a mixed solvent of thethree types of the first to third organic solvents.

When any of the above mixed solvents is used, the polyvinyl chlorideresin and the pigment can be fixed firmly onto the surface of thepolyvinyl chloride sheet, etc., and images, characters, etc., ofexcellent water resistance, light resistance, scratch resistance, etc.,can be printed. Also, gelling of the polyvinyl chloride resin in a shortperiod and aggregation and sedimentation of the pigment in a shortperiod can be prevented. Moreover with these mixed solvents, there is nopossibility of degrading the eutectoid coating film in a short period.

As the first to third organic solvents that are mixed, it is preferableto combine and use organic solvents that do not exhibit basicity inparticular, or more specifically, organic solvents with a pH ofapproximately 2 to 9. This is because with such organic solvents that donot exhibit basicity, there is no possibility of promotion of a radicalpolymerization reaction of unreacted monomer as described above orinhibition of the function of the radical polymerization inhibitor.

(First Organic Solvent)

One type or two or more types among ethylene glycol dimethyl ether,diethylene glycol dimethyl ether, diethylene glycol ethyl methyl ether(pH=6.8), etc.

(Second Organic Solvent)

One type or two or more types among diethylene glycol diethyl ether(pH=4.0), diethylene glycol isopropyl methyl ether, diethylene glycolbutyl methyl ether, tetraethylene glycol dimethyl ether (pH=6.7),propylene glycol dimethyl ether (pH=2.6), etc.

(Third Organic Solvent)

One type or two or more types among ethylene glycol monomethyl ether,ethylene glycol monobutyl ether (pH=4.9), diethylene glycol monoethylether (pH=7.6), diethylene glycol monobutyl ether, diethylene glycoldibutyl ether, triethylene glycol monomethyl ether (pH=7.8), triethyleneglycol monoethyl ether, triethylene glycol monobutyl ether, triethyleneglycol butyl methyl ether, propylene glycol monomethyl ether, propyleneglycol monobutyl ether (pH=6.9), isopropylene glycol monomethyl ether,dipropylene glycol monomethyl ether (pH=5.8), dipropylene glycolmonoethyl ether, dipropylene glycol monobutyl ether, dipropylene glycoldimethyl ether (pH=3.5), tripropylene glycol monomethyl ether,tripropylene glycol dimethyl ether (pH=7.2), etc.

The above classification of the first to third organic solvents is basedon a classification method described in JP2009-74034A.

That is, the first organic solvent is an organic solvent having both adissolving ability as described in (1) below and a swelling ability asdescribed in (2), the second organic solvent is an organic solvent nothaving the dissolving ability as described in (1) but having theswelling ability as described in (2), and the third organic solvent isan organic solvent having neither the dissolving ability as described in(1) nor the swelling ability as described in (2).

(1) Dissolving Ability Test

If after adding 0.2 g of a vinyl chloride-vinyl acetate copolymer [VYHD,made by The Dow Chemical Company, number average molecular weightMn=22000, vinyl acetate content 14 mass %] to 20 ml of an organicsolvent and performing stirring for 1 hour at 25±1° C., the entireamount of the copolymer could be dissolved (the solution becametransparent), the organic solvent was evaluated as having a dissolvingability and if the entire amount of the copolymer could not be dissolved(the solution became turbid and solids precipitated) the organic solventwas evaluated as not having the dissolving ability.

A detailed procedure of the dissolving ability test is as follows.

20 ml of the organic solvent to be evaluated is placed in a beaker, astirring element with a surface coated with Teflon (registeredtrademark) is placed in the beaker, and a temperature is stabilized byleaving the beaker to stand in a constant temperature bath set at 25±1°C.

A magnetic stirrer is then operated to rotate the stirring element andstirring is performed under a condition of a rotation speed of no lessthan 500 rpm and no more than 1000 rpm.

While stirring, 0.2 g of the powder-form vinyl chloride-vinyl acetatecopolymer are added and after continuing to stir further for 1 hour, thesolution is observed visually.

Then, as described above, the organic solvent with which the solutionbecame transparent is evaluated as having the dissolving ability andthat with which the solution became turbid and solids precipitated wasevaluated as not having the dissolving ability.

(2) Swelling Ability Test

An unplasticized vinyl chloride pipe (VP) (JIS K67427922, Eslon pipe forwater supply VP25 R00074261) defined in Japanese Industrial StandardsJIS K6742:2004 and having a standard outer diameter dimension of 32.0 mmand a nominal inner diameter of 25 mm is immersed in the organicsolvent, and after leaving to stand for 3 days at 60±1° C., a rate ofchange of the inner diameter is measured, and an organic solvent withwhich the rate of change is no less than 1% is evaluated as having aswelling ability and an organic solvent with which the rate of change isless than 1% is evaluated as not having the swelling ability.

A detailed procedure of the swelling ability test is as follows.

300 ml of the organic solvent to be evaluated are placed in a beaker andthe beaker is left to stand in a constant temperature bath set at 60°C.±1° C. to stabilize the temperature.

The unplasticized vinyl chloride pipe (VP), which has been cut to alength of 80 mm in advance and the inner diameter of which has beenmeasured, is then immersed in the organic solvent, and after leaving tostand for 3 days, the pipe is taken out of the organic solvent and theinner diameter is measured immediately.

An organic solvent with which the rate of change of inner diameterbefore and after immersion is no less than 1% is then evaluated ashaving the swelling ability and that with which the rate of change isless than 1% is evaluated as not having the swelling ability.

When the two types of the first and second organic solvents among thethree types of the organic solvents are used in combination, thepolyvinyl chloride resin can be dissolved satisfactorily without causingdegradation of the eutectoid coating film, etc., in a short period.

That is, the first organic solvent is a good solvent for the polyvinylchloride resin but is not as strong in dissolving ability as an aproticpolar solvent. The second organic solvent is even weaker in dissolvingability. Thus, with the mixed solvent of these two types of organicsolvent, there is no possibility of degradation of the eutectoid coatingfilm, etc., in a short period.

Moreover with the mixed solvent, the polyvinyl chloride resin dissolvingability of the first organic solvent can be compensated by the swellingaction by the second organic solvent, and the polyvinyl chloride resindissolving ability can thereby be improved to a level approximatelyequivalent to that of an aprotic polar solvent.

Thus, in combination with the molecular structures of the first andsecond organic solvents being mutually similar, effects of improving astorage stability of the non-aqueous inkjet ink and preventingaggregation and sedimentation of the polyvinyl chloride resin and thepigment in a short period can be provided.

Also, a permeability of the non-aqueous inkjet ink with respect to thepolyvinyl chloride sheet, etc., can be improved to enable the polyvinylchloride resin and pigment to be fixed firmly to the surface of thepolyvinyl chloride sheet, etc.

Further, the third organic solvent can be used in combination to adjusta surface tension, viscosity, etc., of the non-aqueous inkjet ink in arange suited for inkjet printing.

In the mixed solvent combining the two types of the first and secondorganic solvents, the content proportion of the first organic solventwith respect to the total amount of the mixed solvent is preferably noless than 5 mass % and especially preferably no less than 8 mass %, andpreferably no more than 50 mass % and especially preferably no more than40 mass %.

When the content proportion is less than the above range, the effect dueto the first organic solvent of improving the polyvinyl chloride resindissolving ability and improving the storage stability of thenon-aqueous inkjet ink may not be obtained adequately. Also, the effectof increasing the permeability to fix the polyvinyl chloride resin andthe pigment firmly onto the surface of the polyvinyl chloride sheet,etc., may not be obtained adequately.

On the other hand, when the content proportion exceeds the above range,the dissolving ability of the mixed solvent may become too strong sothat especially when solid printing is performed on the surface of thepolyvinyl chloride sheet, etc., the surface may become roughened andluster, smoothness, etc., of the print may decrease.

In the mixed solvent combining the three types of the first to thirdorganic solvents, the content proportion of the first organic solventwith respect to the total amount of the mixed solvent is preferably noless than 5 mass % and especially preferably no less than 8 mass %, andpreferably no more than 50 mass % and especially preferably no more than40 mass %. The reasons for this are the same as those in the case of themixed solvent combining the two types of the first and second organicsolvents.

Also, the content proportion of the third organic solvent with respectto the total amount of the mixed solvent is preferably no less than 1mass % and especially preferably no less than 2 mass %, and preferablyno more than 50 mass % and especially preferably no more than 40 mass %.

When the content proportion is less than the above range, the action dueto containing of the third solvent of adjusting the surface tension,viscosity, etc., may not be obtained adequately.

Also, depending on the types and content proportions of the first andsecond organic solvents, the dissolving ability of the mixed solvent maybe too strong so that especially when solid printing is performed on thesurface of the polyvinyl chloride sheet, etc., the surface may becomeroughened and the luster, smoothness, etc., of the print may decrease.

On the other hand, when the content proportion exceeds the above range,the content proportions of the first and second organic solvents becometoo low relatively. Thus, the effect due to the first organic solvent ofimproving the polyvinyl chloride resin dissolving ability and the effectdue to the second organic solvent of assisting the action of the firstorganic solvent may be inadequate.

As a result, the effect of improving the storage stability of thenon-aqueous inkjet ink and the effect of increasing the permeability tofix the polyvinyl chloride resin and the pigment firmly onto the surfaceof the polyvinyl chloride sheet, etc., may not be obtained adequately.

Of the various components making up the non-aqueous inkjet ink, the pHof the components that are liquids in themselves, such as the organicsolvent, etc., shall be expressed as a value measured by a glasselectrode method.

That is, the pH is determined from a potential difference arising acrossa glass electrode and a reference electrode when both electrodes areimmersed in a liquid to be measured under an environment of 25±1° C.temperature. A 3 mol/1 aqueous KCl solution is used as an internalliquid inside the glass electrode.

The pH of a solid component in a case where the component iswater-soluble shall be expressed as the value measured by the glasselectrode method under an environment of 25±1° C. temperature with thecomponent being put in a state of a 5% aqueous solution by dissolving inpure water. The 3 mol/1 aqueous KCl solution is used as the internalliquid inside the glass electrode.

As an example of an apparatus (pH meter) for pH measurement by the glasselectrode method, HM-40V made by DKK-Toa Corporation, etc., can becited.

As a specific measurement method, the glass electrode and the referenceelectrode are immersed in the liquid to be measured and the pH value isread after an elapse of 1 minute. Particularly in a case of an organicsolvent system, the pH value may not stabilize, and in this case acentral value of fluctuation of the pH value is determined as the pHvalue.

As a preferable example of the mixed solvent, a mixed solvent ofdiethylene glycol ethyl methyl ether as the first organic solvent and atleast one type of the following preferable second organic solvents canbe cited.

(Preferable Second Solvents)

Diethylene glycol diethyl ether, tetraethylene glycol dimethyl ether,and propylene glycol dimethyl ether.

Also, a mixed solvent with which at least one type of the followingpreferable third organic solvent is added to diethylene glycol ethylmethyl ether and at least one type of the preferable second organicsolvents can be cited as a preferable example.

(Preferable Third Solvents)

Ethylene glycol monobutyl ether, diethylene glycol monoethyl ether,triethylene glycol monomethyl ether, propylene glycol monobutyl ether,dipropylene glycol monomethyl ether, dipropylene glycol dimethyl ether,and tripropylene glycol dimethyl ether.

<Pigment>

As the pigment, any inorganic pigment and/or organic pigment can becited.

Titanium oxide, iron oxide, and other metal compounds, and neutral,acidic, basic, and other various carbon blacks manufactured by suchknown methods as a contact method, furnace method, thermal method, etc.,can be cited as examples of the inorganic pigment among the above.

Azo pigments, polycyclic pigments, dye chelates, nitro pigments, nitrosopigments, aniline black, etc., can be cited as examples of organicpigments.

Azo lakes, insoluble azo pigments, condensed azo pigments, chelate azopigments, etc., can be cited as examples of azo pigments.

Phthalocyanine pigments, perylene pigments, perinone pigments,anthraquinone pigments, quinacridone pigments, dioxazine pigments,thioindigo pigments, isoindolinone pigments, quinophthalone pigments,etc., can be cited as examples of polycyclic pigments.

Further, basic dye chelates, acidic dye chelates, etc., can be cited asexamples of dye chelates.

One type or two or more types of pigments may be used according to acolor type of the non-aqueous inkjet ink. Also, the pigment may besurface-treated to improve dispersion stability in the non-aqueousinkjet ink.

The following various pigments can be cited as specific examples of thepigment.

(Cyan Pigment)

C. I. Pigment Blue 1, 2, 3, 15, 15:1, 15:3, 15:4, 15:6, 15:34, 16, 22,and 60.

(Magenta Pigment)

C. I. Pigment Red 5, 7, 9, 12, 48 (Ca), 48 (Mn), 49, 52, 53, 57 (Ca),57:1, 97, 112, 122, 123, 149, 168, 177, 178, 179, 184, 202, 206, 207,209, 242, 254, and 255.

(Yellow Pigment)

C. I. Pigment Yellow 1, 2, 3, 12, 13, 14, 14C, 16, 17, 20, 24, 73, 74,75, 83, 86, 93, 94, 95, 97, 98, 109, 110, 114, 117, 120, 125, 128, 129,130, 137, 138, 139, 147, 148, 150, 151, 154, 155, 166, 168, 180, 185,213, and 214.

(Black Pigment)

C. I. Pigment Black 7.

(Orange Pigment)

C. I. Pigment Orange 36, 43, 51, 55, 59, 61, 71, and 74.

(Green Pigment)

C. I. Pigment Green 7 and 36.

(Violet Pigment)

C. I. Pigment Violet 19, 23, 29, 30, 37, 40, and 50.

The content proportion of the pigment with respect to the total amountof the non-aqueous inkjet ink is preferably no less than 0.1 mass % andespecially preferably no less than 0.4 mass %, and preferably no morethan 10 mass % and especially preferably no more than 8 mass %.

The pigment is preferably used as a manufacturing raw material of thenon-aqueous inkjet ink in a state of a pigment dispersion prepared bydispersing in a suitable solvent.

As the solvent making up the pigment dispersion, any of various solventsthat are soluble in the organic solvent making up the non-aqueous inkjetink and are yet capable of satisfactorily dispersing the pigment may beused. For example, when the organic solvent is a combined system of twoor more types among the three types of the first to third organicsolvents, one type or two or more types of the three types of organicsolvents is or are favorably used as the solvent making up the pigmentdispersion.

Also, the pigment dispersion may contain various additives such as adispersing agent for satisfactorily dispersing the pigment.

The pH of the pigment dispersion is preferably approximately 2 to 9 toprevent promotion of the radical polymerization reaction of theunreacted monomer or inhibition of the function of the radicalpolymerization inhibitor. For adjustment of the pH of the pigmentdispersion within the above range, the type, amount, combination, etc.,of the solvent, pigment, dispersing agent, etc., are selected as suited.

<Radical Polymerization Inhibitor>

As the radical polymerization inhibitor, any of various compounds havinga function of trapping radicals and thereby inhibiting the radicalpolymerization reaction of the unreacted monomer contained in thepolyvinyl chloride resin may be used.

However, a radical polymerization inhibitor that does not inhibit adischargeability of the non-aqueous inkjet ink and yet is excellent inefficiency of polymerization inhibition effect is preferable.

The efficiency of polymerization inhibition effect refers to the contentproportion of the radical polymerization inhibitor required to expressthe effect of inhibiting the radical polymerization reaction of theunreacted monomer at a fixed level. It can be said that the lower thiscontent proportion, the higher the efficiency of polymerizationinhibition effect.

A radical polymerization inhibitor that can efficiently inhibit theradical polymerization reaction of the monomer and suppress gelling ofthe polyvinyl chloride resin by being contained at as low an amount aspossible is preferable.

Especially in a case of using the mixed solvent of the two types of thefirst and second organic solvents or the mixed solvent of the threetypes of the first to third organic solvents that is not as strong indissolving ability as an aprotic polar organic solvent as describedabove, it is preferable to select and use a radical polymerizationinhibitor of excellent efficiency of polymerization inhibition effectthat provides a high polymerization inhibition effect at as low anaddition amount as possible.

Satisfactory dissolution of the polyvinyl chloride resin can thereby bemaintained while minimizing decrease of the content proportion of themixed solvent due to the containing of the radical polymerizationinhibitor.

As the radical polymerization inhibitor that meets these conditions, onetype or two or more types among hydroquinones, catechols, hinderedamines, phenols, phenothiazines, and condensed aromatic ring quinonescan be cited as examples.

As examples of hydroquinones, one type or two or more types amonghydroquinone, hydroquinone monomethyl ether,1-o-2,3,5-trimethylolhydroquinone, 2-tert-butylhydroquinone, etc., canbe cited.

As examples of catechols, one type or two or more types among catechol,4-methylcatechol, and 4-tert-butylcatechol, etc., can be cited.

As examples of hindered amines, any of hindered amines having apolymerization inhibition effect can be cited, and among these, one typeor two or more types of hindered amine having a tetramethylpiperidinylgroup in the molecule is or are preferable.

As examples of phenols, one type or two or more types among phenol,butylhydroxytoluene, butylhydroxyanisole, pyrogallol, alkyl esters ofgallic acid, hindered phenols, etc., can be cited.

As examples of phenothiazines, phenothiazine, etc., can be cited.

Further as examples of condensed aromatic ring quinones, naphthoquinone,etc., can be cited.

Among the above, hindered amines and/or hindered phenols, which areespecially excellent in the efficiency of polymerization inhibitioneffect, are used favorably as radical polymerization inhibitors.

As the hindered amines,4,4′-[(1,10-dioxo-1,10-decanediyl)bis(oxy)]bis[2,2,6,6-tetramethyl]-1-piperidinyloxy[alternative name: bis(2,2,6,6-tetramethyl-1-piperidinyloxy-4-yl)sebacate, Irgastab (registered trademark) UV10 made by Ciba SpecialtyChemicals Corp. or equivalent product], etc., are especially preferable.

As examples of the hindered phenols, a mixture in whichα,α′,α″-1,2,3-propanetriyltris[ω[(1-oxo-2-propene-1-yl)oxy]]-poly[oxy(methyl-1,2-ethanediyl)] has2,6-bis(1,1-dimethylethyl)-4-(phenylmethylene)-2,5-cyclohexadine-1-onemixed therein as an effective component [Irgastab UV22 made by CibaSpecialty Chemicals Corp. (mixture with the proportion of the formerbeing 76 to 90 mass % and the proportion of the latter being 24 to 10mass %)], etc., are preferable.

The efficiency of polymerization inhibition effect varies greatly notonly according to the type of the radical polymerization inhibitor butalso according to the types of other components combined with theradical polymerization inhibitor, especially the pigment. Although thereason for this is not clear, it is considered that a structure of achromogenic group, etc., contained in the pigment has an effect.

That is, a mechanism by which the radical polymerization reaction isinhibited differs according to the type of the radical polymerizationinhibitor, and it is considered that whether a favorable effect orunfavorable effect is applied to the different mechanisms differsaccording to the type of the pigment, that is, according to thestructure of the chromogenic group, etc.

It is thus preferable that, in accordance with the type of the pigmentused, a radical polymerization inhibitor, with which the efficiency ofpolymerization inhibition effect is maximized when combined with thepigment, is contained at an optimal range.

For example, the following pigment and radical polymerization inhibitorcombinations may be considered for inks of the respective colors ofcyan, magenta, yellow, and black that are used in combination to form afull-color image on the surface of the polyvinyl chloride sheet, etc.

<Cyan Ink>

In a cyan non-aqueous inkjet ink using a phthalocyanine pigment, such asC. I. Pigment Blue 15, 15:1, 15:3, 15:4, 15:6, 15:34, etc., a hinderedamine is preferably used as the radical polymerization inhibitor.

Also, as the hindered amine, Irgastab UV10 or an equivalent product ispreferably used.

The content proportion of the hindered amine with respect to the totalamount of the non-aqueous inkjet ink is preferably no less than 0.2 mass% and especially preferably no less than 0.5 mass %, and preferably nomore than 2 mass % and especially preferably no more than 1.5 mass %.

When the content proportion is below the above range, the effect due tothe hindered amine of inhibiting the radical polymerization reaction andpreventing the gelling of the polyvinyl chloride resin may not beobtained adequately.

On the other hand, when the above range is exceeded, a further effect isnot obtained and in addition, the excess hindered amine may inhibitcolor expression by the pigment and change a hue of an image orcharacter printed on the surface of the polyvinyl chloride sheet, etc.

Also, many of the hindered amines take a form of a brown powder at roomtemperature.

Thus, when a large amount of the hindered amine is contained in excessof the above range, the viscosity of the non-aqueous inkjet ink becomestoo high and it may not be possible to satisfactorily discharge thenon-aqueous inkjet ink as droplets through the nozzle of the inkjetprinter.

Further, the excess hindered amine may precipitate and decrease thefixing property of the print and decrease the image quality.

<Magenta Ink>

In a magenta non-aqueous inkjet ink using a quinacridone pigment, suchas C. I. Pigment Red 122, etc., a hindered phenol is preferably used asthe radical polymerization inhibitor.

Also, as the hindered phenol, Irgastab UV22 is preferably used.

The content proportion of the hindered phenol with respect to the totalamount of the non-aqueous inkjet ink is preferably no less than 0.05mass % and especially preferably no less than 0.1 mass %, and preferablyno more than 2 mass % and especially preferably no more than 1 mass %.

When the content proportion is below the above range, the effect due tothe hindered phenol of inhibiting the radical polymerization reactionand preventing the gelling of the polyvinyl chloride resin may not beobtained adequately.

On the other hand, when the above range is exceeded, a further effect isnot obtained and in addition, the excess hindered phenol may inhibitcolor expression by the pigment and change the hue of an image orcharacter printed on the surface of the polyvinyl chloride sheet, etc.

Also, many of the hindered phenols take a form of a viscous yellowliquid at room temperature.

Thus, when a large amount of the hindered phenol is contained in excessof the above range, the viscosity of the inkjet ink becomes too high andit may not be possible to satisfactorily discharge the non-aqueousinkjet ink as droplets through the nozzle of the inkjet printer.

Further, the excess hindered phenol may precipitate and decrease thefixing property of the print and decrease the image quality.

<Yellow Ink>

In a yellow non-aqueous inkjet ink using a chelate azo pigment, such asC. I. Pigment Yellow 150, etc., a hindered amine is preferably used asthe radical polymerization inhibitor.

Also, as the hindered amine, Irgastab UV10 or an equivalent product ispreferably used.

The content proportion of the hindered amine with respect to the totalamount of the non-aqueous inkjet ink is preferably no less than 0.05mass % and especially preferably no less than 0.1 mass %, and preferablyno more than 2 mass % and especially preferably no more than 0.5 mass %.

The reasons why the above range is preferable for the content proportionof the hindered amine are the same as those in the case of the cyannon-aqueous inkjet ink.

<Black Ink>

In a black non-aqueous inkjet ink using carbon black as the pigment, ahindered amine is preferably used as the radical polymerizationinhibitor.

Also, as the hindered amine, Irgastab UV10 or an equivalent product ispreferably used.

The content proportion of the hindered amine with respect to the totalamount of the non-aqueous inkjet ink is preferably no less than 0.05mass % and especially preferably no less than 0.1 mass %, and preferablyno more than 2 mass % and especially preferably no more than 0.5 mass %.

The reasons why the above range is preferable for the content proportionof the hindered amine are the same as those in the case of the cyannon-aqueous inkjet ink.

<Metal Coordination Compound>

The non-aqueous inkjet ink according to the present invention maycontain a metal coordination compound.

As described above, the metal coordination compound coordinates to thenickel in the eutectoid coating film and thereby functions to improveresistance of the eutectoid coating film against the organic solvent.

Nitrogen-containing compounds, such as imidazoles, benzotriazoles, etc.,can be cited as examples of the metal coordination compound.

Benzotriazoles are especially preferable as metal coordinationcompounds. In addition to being excellent in function as metalcoordination compounds, the benzotriazoles do not exhibit basicity andthus do not have a possibility of promoting a radical polymerizationreaction.

As specific examples of the benzotriazoles,1-[N,N-bis(2-ethylhexyl)aminomethyl]benzotriazole, etc., can be cited.This compound is a water-soluble solid and the pH measured with a 5%aqueous solution prepared by dissolving in pure water is 7.5.

The content proportion of the metal coordination compound with respectto the total amount of the non-aqueous inkjet ink is preferably no lessthan 0.1 mass % and especially preferably no less than 0.3 mass %, andpreferably no more than 5 mass % and especially preferably no more than3 mass %.

When the content proportion is below the above range, the effect due tocontaining of the metal coordination compound of improving theresistance of the eutectoid film against the organic solvent may not beobtained adequately.

On the other hand, when the content proportion exceeds the above range,the non-aqueous inkjet ink becomes too high in viscosity and it may notbe possible to satisfactorily discharge the non-aqueous inkjet ink asdroplets through the nozzle of the inkjet printer.

Also, the excess metal coordination compound may precipitate to decreasethe fixing property of the print and decrease the image quality.

<Others>

In addition to the above components, an epoxidized substance fortrapping chlorine produced by dehydrochlorination of the polyvinylchloride resin or any of other various additives, such as a polymerdispersing agent, surfactant, plasticizer, antistatic agent, viscositymodifier, surface tension modifier, leveling agent, antifoaming agent,antioxidant, pH adjuster, ultraviolet absorber, photostabilizer,fungicide, biocidal agent, etc., may be contained as necessary atsuitable proportions in the non-aqueous inkjet ink.

<<Ink Set>>

The present invention provides an ink set that is used in an inkjetprinter, is used to form, for example, a full-color image on a surfaceof a polyvinyl chloride sheet, etc., includes non-aqueous inkjet inks atleast of respective colors of cyan, magenta, yellow, and black, and ischaracterized in that the non-aqueous inkjet ink of at least one of therespective colors is the non-aqueous inkjet ink according to the presentinvention.

The polyvinyl chloride resin that is synthesized by the suspensionpolymerization method or the emulsion polymerization method and iscontained in the non-aqueous inkjet ink is thereby prevented fromgelling in a short period and causing a discharge fault, clogging, etc.,upon being vacuum filled and stored in a bag made, for example, of analuminum laminate material, etc.

In particular, the gelling occurs most readily in a cyan non-aqueousinkjet ink that contains a phthalocyanine pigment and is least likely tooccur in a yellow non-aqueous inkjet ink that contains a chelate azopigment. Although the reason for this is not clear, it is consideredthat the structure of the pigment has an effect.

Thus, with the ink set, at least the cyan ink should be the non-aqueousinkjet ink according to the present invention. That is, a radicalpolymerization inhibitor should be contained in the cyan non-aqueousinkjet ink.

However, in consideration of reliably preventing gelling in thenon-aqueous inkjet inks of the other colors to form an image, especiallya full-color image of excellent image quality and color reproducibilityon the surface of the polyvinyl chloride sheet, it is preferable for theinks of all four colors to contain radical polymerization inhibitors andbe the non-aqueous inkjet ink according to the present invention.

In addition to the above four colors, light-color non-aqueous inkjetinks of light cyan, light magenta, light yellow, gray, etc., may becombined in the ink set.

In this case, all of the light-color non-aqueous inkjet inks are low inthe amounts of pigment and polyvinyl chloride resin and are thus lesslikely to gel even in comparison to yellow and thus do not have tocontain radical polymerization inhibitors. However in consideration ofreliably preventing gelling, radical polymerization inhibitors may becontained in the light-color non-aqueous inkjet inks.

EXAMPLES

Preparation, measurement, and testing of non-aqueous inkjet inks of thefollowing examples and comparative examples were carried out under anenvironment of 25±1° C. temperature and 55±1% relative humidity unlessnoted otherwise.

Cyan Ink Example 1

While stirring 18 mass parts of diethylene glycol monoethyl ether(2EG-1E, pH=7.6), 4 mass parts of a vinyl chloride-vinyl acetatecopolymer synthesized by the emulsion polymerization method [VINNOL(registered trademark) E15/45 made by Wacker Chemie AG, weight averagemolecular weight Mw: 45000 to 55000, vinyl acetate content: 15.0±1.0mass %] were added and dispersed as a binder resin, and thereafter 25.3mass parts of diethylene glycol diethyl ether (2EG-2E, pH=4.0) wereadded to swell the copolymer.

Then, while continuing to stir, 22 mass parts of diethylene glycol ethylmethyl ether (2EG-EM, pH=6.8) were added to dissolve the copolymer andthereafter, 0.2 mass parts of4,4-[(1,10-dioxo-1,10-decanediyl)bis(oxy)]bis[2,2,6,6-tetramethyl]-1-piperidinyloxy[product equivalent to Irgastab (registered trademark) UV10 made by CibaSpecialty Chemicals Corp.] as a hindered amine (radical polymerizationinhibitor) and 0.5 mass parts of1-[N,N-bis(2-ethylhexyl)aminomethyl]benzotriazole (pH measured in thestate of 5% aqueous solution=7.5) as a metal coordination compound wereadded to prepare a resin solution.

Also, a pigment dispersion was prepared in which C. I. Pigment Blue 15:3was dispersed as a phthalocyanine pigment in diethylene glycol diethylether (pigment concentration 15 mass %, pH=8.6), and 30 mass parts ofthe pigment dispersion were added to 70 mass parts of the resin solutionprepared in advance and further stirring was performed to form a uniformphase and thereby manufacture a non-aqueous inkjet ink.

Example 2

Besides setting the amount of the hindered amine in the resin solutionto 0.5 mass parts and the amount of diethylene glycol diethyl ether to25 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 1.

Example 3

Besides setting the amount of the hindered amine in the resin solutionto 1 mass part and the amount of diethylene glycol diethyl ether to 24.5mass parts, a non-aqueous inkjet ink was manufactured in the same manneras in Example 1.

Example 4

Besides setting the amount of the hindered amine in the resin solutionto 1.5 mass parts and the amount of diethylene glycol diethyl ether to24 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 1.

Example 5

Besides setting the amount of the hindered amine in the resin solutionto 2 mass parts and the amount of diethylene glycol diethyl ether to23.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 1.

Comparative Example 1

Besides not adding the hindered amine to the resin solution and settingthe amount of diethylene glycol diethyl ether to 25.5 mass parts, anon-aqueous inkjet ink was manufactured in the same manner as in Example1.

<Storage Property Test>

Approximately 50 g of each of the non-aqueous inkjet inks manufacturedin Examples 1 to 5 and Comparative Example 1 were injected into a bag(approximately 8 cm long×approx. 9 cm wide) made of an aluminum laminatematerial and vacuum filling was performed, that is, an interior of thebag was degassed and then heat sealing was performed.

The bag was then left to stand under an environment of 90±1° C. toreproduce a thermal history during storage, which is considered to beone of triggers that start the radical polymerization reaction, and thenopened four days later to determine, from a change of viscosity of thenon-aqueous inkjet ink, whether or not the radical polymerizationreaction occurred. That is, the viscosity of each non-aqueous inkjet inkwas measured under conditions of 25±1° C. and 20 rpm before filling intothe bag and after taking out from the bag and the difference inviscosity was determined to evaluate whether or not the radicalpolymerization reaction occurred according to the following standards.

Excellent: The difference in viscosity was less than 1.0 mPa·s and itwas judged that the radical polymerization reaction did not proceed atall.

Good: The difference in viscosity was no less than 1.0 mPa·s and no morethan 1.5 mPa·s and it was judged that the radical polymerizationreaction hardly proceeded.

Normal: The difference in viscosity was no less than 1.5 mPa·s and nomore than 2.0 mPa·s and it was judged that although the radicalpolymerization reaction proceeded, there are no problems in terms ofpractical use.

Poor: The difference in viscosity was no less than 2.0 mPa·s or gellingof the polyvinyl chloride resin occurred and it was judged that theradical polymerization reaction proceeded.

<Hue Difference Evaluation>

Approximately 0.5 ml of each of the non-aqueous inkjet inks manufacturedin Examples and Comparative Example were dropped onto a surface of apolyvinyl chloride sheet and after coating the ink onto the surface ofthe polyvinyl chloride sheet using a wire bar (0.1 mm diameter), hot airwas blown on for approximately 20 seconds using a hairdryer, andthereafter the sheet was left to stand for 10 minutes at 25±1° C. tothereby prepare a drawdown sample.

A hue of the drawdown sample was measured using a handy typespectrophotometric color difference meter [NF999 made by Nippon DenshokuIndustries Co., Ltd.]. With each drawdown sample, measurements were madeat three locations and an average value was determined. A hue differenceΔE with respect to the drawdown sample formed using the non-aqueousinkjet ink of Comparative Example 1 that does not contain thepolymerization inhibitor was determined, and whether a deviation of thehue was large or small was evaluated according to the followingstandards.

Good: The ΔE was less than 1.0 and it was judged that there was nodeviation of hue.

Normal: The ΔE was no less than 1.0 and less than 1.5 and it was judgedthat although the hue deviated slightly, there are no problems in termsof practical use.

Poor: The ΔE was no less than 1.5 and it was judged that deviation ofhue occurred.

The results of the above are shown in Table 1.

TABLE 1 Comparative Example 1 Example 2 Example 3 Example 4 Example 5Example 1 Mass parts Cyan pigment dispersion (pH = 8.6) 30 30 30 30 3030 Organic 2EG-EM (pH = 6.8) 22 22 22 22 22 22 solvent 2EG-2E (pH = 4.0)25.3 25 24.5 24 23.5 25.5 2EG-1E (pH = 7.6) 18 18 18 18 18 18N-methyl-2-pyrrolidone — — — — — — (pH = 11.7) Radical UV10 0.2 0.5 11.5 2 — Polymerization (hindered amine compound) inhibitor UV22 — — — —— — (hindered phenol compound) Binder resin VINNOL E15/45 4 4 4 4 4 4(emulsion polymerization) SOLBIN CL — — — — — — (suspensionpolymerization) Metal 2-methylimidazole — — — — — — Coordination (pH =11.0) compound 1-[N,N-bis(2-ethylhexyl) 0.5 0.5 0.5 0.5 0.5 0.5aminomethyl]benzotriazole (pH = 7.5) Evaluation Storage property NormalExcellent Excellent Excellent Excellent Poor Hue difference ΔE Good GoodGood Good Normal Reference

From the results for Examples 1 to 5 and Comparative Example 1 shown inTable 1, it was found that by making the cyan non-aqueous inkjet inkthat uses the phthalocyanine pigment as the pigment contain a hinderedamine as the radical polymerization inhibitor, the radicalpolymerization reaction of the unreacted monomer and the accompanyinggelling of the polyvinyl chloride resin can be prevented.

Also, from the results for Examples 1 to 5, it was found that in thecyan non-aqueous inkjet ink, the content proportion of the hinderedamine with respect to the total amount of the non-aqueous inkjet ink ispreferably no less than 0.2 mass % and especially preferably no lessthan 0.5 mass %, and preferably no more than 2 mass % and especiallypreferably no more than 1.5 mass %.

Example 6

As the binder resin, a vinyl chloride-vinyl acetate copolymersynthesized by the suspension polymerization method [SOLBIN (registeredtrademark) CL manufactured by Nissin Chemical Industry Co., Ltd., numberaverage molecular weight Mn: 25000, vinyl acetate content: 14 mass] wasused in place of the vinyl chloride-vinyl acetate copolymer synthesizedby the emulsion polymerization method.

Also, besides adding 4 mass parts of the vinyl chloride-vinyl acetatecopolymer to the resin solution and setting the amount of the hinderedamine to 1 mass part and the amount of diethylene glycol diethyl etherto 24.5 mass parts, a non-aqueous inkjet ink was manufactured in thesame manner as in Example 1.

Comparative Example 2

Besides not adding the hindered amine to the resin solution and settingthe amount of diethylene glycol diethyl ether to 25.5 mass parts, anon-aqueous inkjet ink was manufactured in the same manner as in Example6.

Example 7

As the metal coordination compound, 2-methylimidazole (pH=11.0) was usedin place of 1-[N,N-bis(2-ethylhexyl)aminomethyl]benzotriazole.

Also, besides adding 0.5 mass parts of the 2-methylimidazole to theresin solution and setting the amount of the hindered amine to 1 masspart and the amount of diethylene glycol diethyl ether to 24.5 massparts, a non-aqueous inkjet ink was manufactured in the same manner asin Example 1.

Example 8

N-methyl-2-pyrrolidone (pH=11.7) was used in place of diethylene glycolethyl methyl ether.

Also, besides adding 22 mass parts of the N-methyl-2-pyrrolidone to theresin solution and setting the amount of the hindered amine to 1 masspart and the amount of diethylene glycol diethyl ether to 24.5 massparts, a non-aqueous inkjet ink was manufactured in the same manner asin Example 1.

The storage property test and the hue difference evaluation were carriedout on the non-aqueous inkjet inks manufactured in Examples 6 to 8. Theresults are shown in Table 2.

TABLE 2 Comparative Example 6 Example 7 Example 8 Example 2 Mass partsCyan pigment dispersion (pH = 8.6) 30 30 30 30 Organic 2EG-EM (pH = 6.8)22 22 — 22 Solvent 2EG-2E (pH = 4.0) 24.5 24.5 24.5 25.5 2EG-1E (pH =7.6) 18 18 18 18 N-methyl-2-pyrrolidone — — 22 — (pH = 11.7) RadicalUV10 1 1 1 — Polymerization (hindered amine compound) inhibitor UV22 — —— — (hindered phenol compound) Binder resin VINNOL E15/45 — 4 4 —(emulsion polymerization) SOLBIN CL 4 — — 4 (suspension polymerization)Metal 2-methylimidazole — 0.5 — — Coordination (pH = 11.0) compound1-[N,N-bis(2-ethylhexyl) 0.5 — 0.5 0.5 aminomethyl]benzotriazole (pH =7.5) Evaluation Storage property Excellent Good Good Poor Hue differenceΔE Good Good Good Good

From the results for Examples 1 to 5 and Comparative Example 1 in theprevious Table 1 and the results for Example 6 and Comparative Example 2in Table 2, it was found that equivalent results are obtained usingeither of the resin synthesized by the suspension polymerization methodand the resin synthesized by the emulsion polymerization method as thepolyvinyl chloride resin.

Also, from the results of Examples 1 to 5 and Example 7, it was foundthat a benzotriazole is preferable as the metal coordination compound.

Further, from the results of Examples 1 to 5 and Example 8, it was foundthat it is preferable to use a combination of alkylene glycolderivatives all having a pH of 2 to 9 as the organic solvent, and thatcombined use of diethylene glycol ethyl methyl ether, diethylene glycoldiethyl ether, which is the preferable second solvent, and diethyleneglycol monoethyl ether, which is the preferable third solvent, isespecially preferable.

Example 9

A mixture in whichα,α′,α″-1,2,3-propanetriyltris[ω-[(1-oxo-2-propene-1-yl) oxy]]-poly[oxy(methyl-1,2-ethanediyl)] has2,6-bis(1,1-dimethylethyl)-4-(phenylmethylene)-2,5-cyclohexadine-1-onemixed therein as an effective component [Irgastab UV22 made by CibaSpecialty Chemicals Corp. (mixture of 76 to 90 mass % of the former and24 to 10 mass % of the latter)] was used as a hindered phenol radicalpolymerization inhibitor in place of the hindered amine.

Also, besides adding 1 mass part of the hindered phenol to the resinsolution and setting the amount of diethylene glycol diethyl ether to24.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 1.

Example 10

Besides setting the amount of the hindered phenol in the resin solutionto 1.5 mass parts and the amount of diethylene glycol diethyl ether to24 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 9.

Example 11

Besides setting the amount of the hindered phenol in the resin solutionto 2 mass parts and the amount of diethylene glycol diethyl ether to23.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 9.

Example 12

N-methyl-2-pyrrolidone (pH=11.7) was used in place of diethylene glycolethyl methyl ether.

Also, besides adding 22 mass parts of the N-methyl-2-pyrrolidone to theresin solution and setting the amount of the hindered phenol to 1.5 massparts and the amount of diethylene glycol diethyl ether to 24 massparts, a non-aqueous inkjet ink was manufactured in the same manner asin Example 9.

The storage property test and the hue difference evaluation were carriedout on the non-aqueous inkjet inks manufactured in Examples 9 to 12. Theresults are shown in Table 3.

TABLE 3 Example 9 Example 10 Example 11 Example 12 Mass parts Cyanpigment dispersion (pH = 8.6) 30 30 30 30 Organic 2EG-EM (pH = 6.8) 2222 22 — Solvent 2EG-2E (pH = 4.0) 24.5 24 23.5 24 2EG-1E (pH = 7.6) 1818 18 18 N-methyl-2-pyrrolidone — — — 22 (pH = 11.7) Radical UV10 — — —— Polymerization (hindered amine compound) inhibitor UV22 1 1.5 2 1.5(hindered phenol compound) Binder resin VINNOL E15/45 4 4 4 4 (emulsionpolymerization) SOLBIN CL — — — — (suspension polymerization) Metal2-methylimidazole — — — — Coordination (pH = 11.0) compound1-[N,N-bis(2-ethylhexyl) 0.5 0.5 0.5 0.5 aminomethyl]benzotriazole (pH =7.5) Evaluation Storage property Normal Good Good Normal Hue differenceΔE Good Good Normal Good

From the results for Examples 1 to 5 in the previous Table 1 and theresults for Examples 9 to 12 in Table 3, it was found that with the cyannon-aqueous inkjet ink, although a hindered phenol can be used as theradical polymerization inhibitor, a hindered amine is more effective interms of the effect of inhibiting the radical polymerization reaction ofthe unreacted monomer and preventing the gelling of the polyvinylchloride resin.

Also, from the results of Examples 9 to 11 and Example 12, it was foundthat even in the non-aqueous inkjet ink using a hindered phenol, it ispreferable to use a combination of alkylene glycol derivatives allhaving a pH of 2 to 9 as the organic solvent and that combined use ofdiethylene glycol ethyl methyl ether, diethylene glycol diethyl ether,which is the preferable second solvent, and diethylene glycol monoethylether, which is the preferable third solvent, is especially preferable.

Magenta Ink Example 13

While stirring 18 mass parts of diethylene glycol monoethyl ether(2EG-1E, pH=7.6), 4 mass parts of a vinyl chloride-vinyl acetatecopolymer synthesized by the emulsion polymerization method [VINNOL(registered trademark) E15/45 made by Wacker Chemie AG, weight averagemolecular weight Mw: 45000 to 55000, vinyl acetate content: 15.0±1.0mass %] were added and dispersed as a binder resin, and thereafter 25.45mass parts of diethylene glycol diethyl ether (2EG-2E, pH=4.0) wereadded to swell the copolymer.

Then, while continuing to stir, 22 mass parts of diethylene glycol ethylmethyl ether (2EG-EM, pH=6.8) were added to dissolve the copolymer, andthereafter, 0.05 mass parts of the mixture in whichα,α′,α″-1,2,3-propanetriyltris[ω-[(1-oxo-2-propene-1-yl)oxy]]-poly[oxy(methyl-1,2-ethanediyl)] has2,6-bis(1,1-dimethylethyl)-4-(phenylmethylene)-2,5-cyclohexadine-1-onemixed therein as the effective component [Irgastab UV22 made by CibaSpecialty Chemicals Corp. (mixture of 76 to 90 mass % of the former and24 to 10 mass % of the latter)] as a hindered phenol (radicalpolymerization inhibitor) and 0.5 mass parts of1-[N,N-bis(2-ethylhexyl)aminomethyl]benzotriazole (pH measured in thestate of 5% aqueous solution=7.5) as a metal coordination compound wereadded to prepare a resin solution.

A pigment dispersion was prepared in which C. I. Pigment Red 122 wasdispersed as a quinacridone pigment in diethylene glycol diethyl ether(pigment concentration 15 mass %, pH=7.6), and 30 mass parts of thepigment dispersion were added to 70 mass parts of the resin solutionprepared in advance and further stirring was performed to form a uniformphase and thereby manufacture a non-aqueous inkjet ink.

Example 14

Besides setting the amount of the hindered phenol in the resin solutionto 0.1 mass parts and the amount of diethylene glycol diethyl ether to25.4 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 13.

Example 15

Besides setting the amount of the hindered phenol in the resin solutionto 0.5 mass parts and the amount of diethylene glycol diethyl ether to25 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 13.

Example 16

Besides setting the amount of the hindered phenol in the resin solutionto 1 mass part and the amount of diethylene glycol diethyl ether to 24.5mass parts, a non-aqueous inkjet ink was manufactured in the same manneras in Example 13.

Example 17

Besides setting the amount of the hindered phenol in the resin solutionto 2 mass parts and the amount of diethylene glycol diethyl ether to23.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 13.

Example 18

4,4′-[(1,10-dioxo-1,10-decanediyl)bis(oxy)]bis[2,2,6,6-tetramethyl]-1-piperidinyloxy [product equivalent to Irgastab(registered trademark) UV10 made by Ciba Specialty Chemicals Corp.] wasused as a hindered amine radical polymerization inhibitor in place ofthe hindered phenol.

Also, besides adding 1 mass part of the hindered amine to the resinsolution and setting the amount of diethylene glycol diethyl ether to24.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 13.

The storage property test and the hue difference evaluation were carriedout on the non-aqueous inkjet inks manufactured in Examples 13 to 18.For the hue difference evaluation, a drawdown sample formed using aseparately-prepared magenta non-aqueous inkjet ink that does not containa polymerization inhibitor was used as a reference. The results areshown in Table 4.

TABLE 4 Example 13 Example 14 Example 15 Example 16 Example 17 Example18 Mass parts Magenta pigment dispersion (pH = 7.6) 30 30 30 30 30 30Organic 2EG-EM (pH = 6.8) 22 22 22 22 22 22 solvent 2EG-2E (pH = 4.0)25.45 25.4 25 24.5 23.5 24.5 2EG-1E (pH = 7.6) 18 18 18 18 18 18N-methyl-2-pyrrolidone — — — — — — (pH = 11.7) Radical UV10 — — — — — 1Polymerization (hindered amine compound) inhibitor UV22 0.05 0.1 0.5 1 2— (hindered phenol compound) Binder resin VINNOL E15/45 4 4 4 4 4 4(emulsion polymerization) SOLBIN CL — — — — — — (suspensionpolymerization) Metal 2-methylimidazole — — — — — — Coordination (pH =11.0) compound 1-[N,N-bis(2-ethylhexyl) 0.5 0.5 0.5 0.5 0.5 0.5aminomethyl]benzotriazole (pH = 7.5) Evaluation Storage property NormalExcellent Excellent Excellent Excellent Normal Hue difference ΔE GoodGood Good Good Normal Good

From the results for Examples 13 to 17 and Example 18 in Table 4, it wasfound that with the magenta non-aqueous inkjet ink using thequinacridone pigment as the pigment, although a hindered amine can beused as the radical polymerization inhibitor, a hindered phenol is moreeffective in terms of the effect of inhibiting the radicalpolymerization reaction of the unreacted monomer and preventing thegelling of the polyvinyl chloride resin.

Also, from the results of Examples 13 to 17, it was found that in themagenta non-aqueous inkjet ink, the content proportion of the hinderedphenol with respect to the total amount of the non-aqueous inkjet ink ispreferably no less than 0.05 mass % and especially preferably no lessthan 0.1 mass %, and preferably no more than 2 mass % and especiallypreferably no more than 1 mass %.

Yellow Ink Example 19

While stirring 18 mass parts of diethylene glycol monoethyl ether(2EG-1E, pH=7.6), 4 mass parts of a vinyl chloride-vinyl acetatecopolymer synthesized by the emulsion polymerization method [VINNOL(registered trademark) E15/45 made by Wacker Chemie AG, weight averagemolecular weight Mw: 45000 to 55000, vinyl acetate content: 15.0±1.0mass %] were added and dispersed as a binder resin, and thereafter 25.45mass parts of diethylene glycol diethyl ether (2EG-2E, pH=4.0) wereadded to swell the copolymer.

Then, while continuing to stir, 22 mass parts of diethylene glycol ethylmethyl ether (2EG-EM, pH=6.8) were added to dissolve the copolymer, andthereafter, 0.05 mass parts of4,4′-[(1,10-dioxo-1,10-decanediyl)bis(oxy)]bis[2,2,6,6-tetramethyl]-1-piperidinyloxy[product equivalent to Irgastab (registered trademark) UV10 made by CibaSpecialty Chemicals Corp.] as a hindered amine (radical polymerizationinhibitor) and 0.5 mass parts of1-[N,N-bis(2-ethylhexyl)aminomethyl]benzotriazole (pH measured in thestate of 5% aqueous solution=7.5) as a metal coordination compound wereadded to prepare a resin solution.

A pigment dispersion was prepared in which C. I. Pigment Yellow 150 wasdispersed as a chelate azo pigment in diethylene glycol diethyl ether(pigment concentration 15 mass %, pH=6.5), and 30 mass parts of thepigment dispersion were added to 70 mass parts of the resin solutionprepared in advance and further stirring was performed to form a uniformphase and thereby manufacture a non-aqueous inkjet ink.

Example 20

Besides setting the amount of the hindered amine in the resin solutionto 0.1 mass parts and the amount of diethylene glycol diethyl ether to25.4 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 19.

Example 21

Besides setting the amount of the hindered amine in the resin solutionto 0.3 mass parts and the amount of diethylene glycol diethyl ether to25.2 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 19.

Example 22

Besides setting the amount of the hindered amine in the resin solutionto 0.5 mass parts and the amount of diethylene glycol diethyl ether to25 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 19.

Example 23

Besides setting the amount of the hindered amine in the resin solutionto 2 mass parts and the amount of diethylene glycol diethyl ether to23.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 19.

The storage property test and the hue difference evaluation were carriedout on the non-aqueous inkjet inks manufactured in Examples 19 to 23.For the hue difference evaluation, a drawdown sample formed using aseparately-prepared yellow non-aqueous inkjet ink that does not containa polymerization inhibitor was used as a reference. The results areshown in Table 5.

TABLE 5 Example 19 Example 20 Example 21 Example 22 Example 23 Massparts Yellow pigment dispersion (pH = 6.5) 30 30 30 30 30 Organic 2EG-EM(pH = 6.8) 22 22 22 22 22 Solvent 2EG-2E (pH = 4.0) 25.45 25.4 25.2 2523.5 2EG-1E (pH = 7.6) 18 18 18 18 18 N-methyl-2-pyrrolidone — — — — —(pH = 11.7) Radical UV10 0.05 0.1 0.3 0.5 2 Polymerization (hinderedamine compound) inhibitor UV22 — — — — — (hindered phenol compound)Binder resin VINNOL E15/45 4 4 4 4 4 (emulsion polymerization) SOLBIN CL— — — — — (suspension polymerization) Metal 2-methylimidazole — — — — —Coordination (pH = 11.0) compound 1-[N,N-bis(2-ethylhexyl) 0.5 0.5 0.50.5 0.5 aminomethyl]benzotriazole (pH = 7.5) Evaluation Storage propertyNormal Excellent Excellent Excellent Excellent Hue difference ΔE GoodGood Good Good Normal

From the results for Examples 19 to 23 in Table 5, it was found thatwith the yellow non-aqueous inkjet ink using a chelate azo pigment asthe pigment, the content proportion with respect to the total amount ofthe non-aqueous inkjet ink of the hindered amine as the radicalpolymerization inhibitor is preferably no less than 0.05 mass % andespecially preferably no less than 0.1 mass %, and preferably no morethan 2 mass % and especially preferably no more than 0.5 mass %.

Black Ink Example 24

While stirring 18 mass parts of diethylene glycol monoethyl ether(2EG-1E, pH=7.6), 4 mass parts of a vinyl chloride-vinyl acetatecopolymer synthesized by the emulsion polymerization method [VINNOL(registered trademark) E15/45 made by Wacker Chemie AG, weight averagemolecular weight Mw: 45000 to 55000, vinyl acetate content: 15.0±1.0mass %] were added and dispersed as a binder resin, and thereafter 25.45mass parts of diethylene glycol diethyl ether (2EG-2E, pH=4.0) wereadded to swell the copolymer.

Then, while continuing to stir, 22 mass parts of diethylene glycol ethylmethyl ether (2EG-EM, pH=6.8) were added to dissolve the copolymer, andthereafter, 0.05 mass parts of4,4′-[(1,10-dioxo-1,10-decanediyl)bis(oxy)]bis[2,2,6,6-tetramethyl]-1-piperidinyloxy[product equivalent to Irgastab (registered trademark) UV10 made by CibaSpecialty Chemicals Corp.] as a hindered amine (radical polymerizationinhibitor) and 0.5 mass parts of1-[N,N-bis(2-ethylhexyl)aminomethyl]benzotriazole (pH measured in thestate of 5% aqueous solution=7.5) as a metal coordination compound wereadded to prepare a resin solution.

A pigment dispersion was prepared in which carbon black was dispersed indiethylene glycol diethyl ether (pigment concentration 15 mass %,pH=5.8), and 30 mass parts of the pigment dispersion were added to 70mass parts of the resin solution prepared in advance and furtherstirring was performed to form a uniform phase and thereby manufacture anon-aqueous inkjet ink.

Example 25

Besides setting the amount of the hindered amine in the resin solutionto 0.1 mass parts and the amount of diethylene glycol diethyl ether to25.4 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 24.

Example 26

Besides setting the amount of the hindered amine in the resin solutionto 0.3 mass parts and the amount of diethylene glycol diethyl ether to25.2 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 24.

Example 27

Besides setting the amount of the hindered amine in the resin solutionto 0.5 mass parts and the amount of diethylene glycol diethyl ether to25 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 24.

Example 28

Besides setting the amount of the hindered amine in the resin solutionto 2 mass parts and the amount of diethylene glycol diethyl ether to23.5 mass parts, a non-aqueous inkjet ink was manufactured in the samemanner as in Example 24.

The storage property test and the hue difference evaluation were carriedout on the non-aqueous inkjet inks manufactured in Examples 24 to 28.For the hue difference evaluation, a drawdown sample formed using aseparately-prepared black non-aqueous inkjet ink that does not contain apolymerization inhibitor was used as a reference. The results are shownin Table 6.

TABLE 6 Example 24 Example 25 Example 26 Example 27 Example 28 Massparts Black pigment dispersion (pH = 5.8) 30 30 30 30 30 Organic 2EG-EM(pH = 6.8) 22 22 22 22 22 solvent 2EG-2E (pH = 4.0) 25.45 25.4 25.2 2523.5 2EG-1E (pH = 7.6) 18 18 18 18 18 N-methyl-2-pyrrolidone — — — — —(pH = 11.7) Radical UV10 0.05 0.1 0.3 0.5 2 Polymerization (hinderedamine compound) inhibitor UV22 — — — — — (hindered phenol compound)Binder resin VINNOL E15/45 4 4 4 4 4 (emulsion polymerization) SOLBIN CL— — — — — (suspension polymerization) Metal 2-methylimidazole — — — — —Coordination (pH = 11.0) compound 1-[N,N-bis(2-ethylhexyl) 0.5 0.5 0.50.5 0.5 aminomethyl]benzotriazole (pH = 7.5) Evaluation Storage propertyNormal Excellent Excellent Excellent Excellent Hue difference ΔE GoodGood Good Good Normal

From the results for Examples 24 to 28 in Table 6, it was found thatwith the black non-aqueous inkjet ink using carbon black as the pigment,the content proportion with respect to the total amount of thenon-aqueous inkjet ink of the hindered amine as the radicalpolymerization inhibitor is preferably no less than 0.05 mass % andespecially preferably no less than 0.1 mass %, and preferably no morethan 2 mass % and especially preferably no more than 0.5 mass %.

What is claimed is:
 1. A non-aqueous inkjet ink, comprising: a polyvinylchloride resin synthesized by a suspension polymerization method or anemulsion polymerization method; an organic solvent that is a mixedsolvent comprising diethylene glycol ethyl methyl ether, diethyleneglycol diethyl ether, and diethylene glycol monoethyl ether in which thepolyvinyl chloride resin is dissolved; a pigment; and a radicalpolymerization inhibitor.
 2. The non-aqueous inkjet ink according toclaim 1, wherein the radical polymerization inhibitor is selected fromthe group consisting of hydroquinones, catechols, hindered amines,phenols, phenothiazines, condensed aromatic ring quinones, andcombinations thereof.
 3. The non-aqueous inkjet ink according to claim1, wherein the polyvinyl chloride resin is a vinyl chloride-vinylacetate copolymer, and wherein the vinyl chloride-vinyl acetatecopolymer has a vinyl content that is no less than 1 mass % and no morethan 36 mass %.
 4. The non-aqueous inkjet ink according to claim 1,wherein the non-aqueous inkjet ink further comprises a benzotriazole. 5.The non-aqueous inkjet ink according to claim 1, wherein the pigment isa phthalocyanine pigment, and wherein the radical polymerizationinhibitor is a hindered amine present in an amount based on total amountof the non-aqueous inkjet ink that is no less than 0.2 mass % and nomore than 2 mass %.
 6. The non-aqueous inkjet ink according to claim 1,wherein the pigment is a quinacridone pigment, and wherein the radicalpolymerization inhibitor is a hindered phenol present in an amount basedon total amount of the non-aqueous inkjet ink that is no less than 0.05mass % and no more than 2 mass %.
 7. The non-aqueous inkjet inkaccording to claim 1, wherein the pigment is a chelate azo pigment, andwherein the radical polymerization inhibitor is a hindered amine presentin an amount based on total amount of the non-aqueous inkjet ink that isno less than 0.05 mass % and no more than 2 mass %.
 8. The non-aqueousinkjet ink according to claim 1, wherein the pigment is carbon black,and wherein the radical polymerization inhibitor is a hindered aminepresent in an amount based on total amount of the non-aqueous inkjet inkthat is no less than 0.05 mass % and no more than 2 mass %.
 9. An inkset of inkjet inks, comprising: a combination of non-aqueous inkjet inksaccording to claim 1 having respective colors and including at least: acyan ink having a cyan color; a magenta ink having a magenta color; ayellow ink having a yellow color; and a black ink having a black color.